Lapox® Bisphenol A Based Resins/ Lapox®双酚A环氧树脂
· Liquid/液状
· Semi-Solid/Solid / 半固状/固状

Liquid Epoxy Resins

Name
品名

Description
状态

Epoxy Value/环氧值
eq/ kg

Viscosity/粘度 @ 25 °C mPas

Colour / 颜色Gardner

Comments /
注解

Lapox® B-11

Liquid

液状

5.2 – 5.5

10000 – 12000

Max 2

中粘度,主要用于无溶剂油漆和建筑.

Medium viscosity resin. Used mainly for solvent free coatings and building applications.

Lapox® B-11LV

Liquid

液状

5.2 – 5.5

7500 - 9000

Max1

中粘度,主要用于无溶剂油漆和建筑.

Medium viscosity resin. Used mainly for solvent free coatings and building applications

Lapox® B-13

Liquid

液状

5.10 – 5.40

12000-16000

Max2

高粘度树脂,多种用途。High viscosity resin. General purpose

Lapox® B-21

Liquid

液状

4.15 – 4.4

1300-1700

Max2

低粘度,建议用在建筑方面。Low viscosity. Resin. Recommended for building applications.

Lapox® B-47

Liquid

液状

5.20 – 5.5

450-650

Max 3

低粘度,活性稀释剂改性,Low viscosity. Reactive diluent modified resin. Recommended for heavily filled screeds.

Lapox® B-41

Liquid

液状

5.20 – 5.6

900-1100

Max 3

低粘度,活性稀释剂改性,用于抗溶解油漆。Low viscosity reactive diluent modified resin for solvent free coatings with good solvent resistance.

Lapox® B-42

Liquid

液状

5.00 – 5.5

5000-6500

Max 5

低粘度,建议用于无溶剂油漆,抗化学腐蚀。Low viscosity resin. Recommended for solvent free coatings with high chemical resistance.

Lapox® P-101

Solvent - cut 溶剂稀释

1.90 -2.2(100% resin)

6000-12000

Max 4

将Lapox P-3 稀释为75%二甲苯溶液

75%solvent-cut of Lapox P-3 in xylene.

Lapox® B-89

Smooth paste 平滑糊状

------

10000-20000

------

填充聚合树脂,与K-6固化剂组合,支持碎石。Filled formulated epoxy compound used with hardener K-6, for backing stone crushers.

Lapox® B-44

Paste 糊状

4.30 – 4.80

13000-23000

------

白色涂料聚合树脂,与K-92固化剂组合,用于无溶剂室温固化抗化学腐蚀内衬。Formulated white pigmented epoxy resin used in combination with hardener K-92 for solvent fee, room temperature curing chemical resistant linings.

Lapox® P-91

Liquid

液状

3.5-4.2

16000-22000

------

聚合树脂,与K-91固化剂组合,用于室温固化的灰泥。

Formulated epoxy resin. Recommended in combination with hardener k-91 for making knifing putties, curable at room temperature.

Lapox® A-83

Beige paste

米色糊状

----

30000-50000

---

良好的防水,抗老化性能,以及非常好的绝缘性。Good water resistance, aging resistance and very good electrical insulation properties.

Lapox® A-16

Pale yellow liquid 浅黄色液体

5.3-5.45

8000-12000

Max 2

与K-5组合,用于抗165度高温的黏合剂。With hardener k-5 is a hot setting epoxy adhesive specially designed for joints capable of withstanding an operating temperature of 165 deg c

Lapox® A-38

Beige paste米色糊状

----

50000-90000

----

室温与K-99固化剂混合,形成良好的防水,防油。120度时,粘合良好。Formulated at room temperature with hardener K-99 to give excellent resistance to moisture and oils. Joints perform well at 120 deg c

Lapox® A-31

Translucent liquid半透明液状

----

25000-45000

----

中等强度粘接金属,陶瓷,皮革,橡胶,宝石,木头和塑料。Gives medium-hard bonds to metals, ceramics, leather, vulcanized rubber, gem stones, wood concrete and thermoset plastics.

Lapox® A-35

Pale yellow clear solution.浅黄色透明溶液

------

2400-3600

Max 4

与K-35固化剂组合,形成热固化胶粘剂,即使120度也能保持很高的机械强度。With hardener K-35 forms heat curing epoxy adhesive characterized by outstanding mechanical strength even at 120 deg c.

Lapox® A-555

Liquid 液状

------

75000-125000

Max10

没有硫醇味道的快速胶粘剂,与K-555合用。Fast setting general-purpose adhesive free from mercaptan odour. Used with K-555

Lapox® C-17

Liquid 液状

5.20-5.50

9000-13000

Max2

与酸酐类固化剂组合的浇铸树脂,用于绝缘体,开关等,有高的机械强度和F级的绝缘性能。Casting resin used with anhydride hardeners for making insulators and switchgear components of high mechanical strength, for class ‘F’ Insulation.

Lapox® C-27

Liquid 液状

4.10-4.30

1100-1500

Max 3

低粘度弹力浇铸树脂,建议与先加入的硅微粉和胺类固化剂合用,用于低压电缆的连接。Low viscosity resilient casting resin. Recommended for pre-filled silica formulations with low caking tendency used with amine curing system for low voltage cable joints.

Lapox® C-58

Liquid液状

6.10-6.40

400-600

Max2

低粘度树脂,与胺类和聚肽胺固化剂合用时,能形成高强度的系统。Low viscosity casting resin yielding highly cross-linked systems when used with amine and polyaminoamide hardeners

Lapox® C-57

Liquid液状

5.20-5.60

400-600

Max2

低粘度浇铸树脂,建议与胺类和聚肽胺类固化剂组合用于低压电器。Low viscosity reactive casting resin. Recommended with amine and polyaminoamide curing agents for low voltage electrical and electronic applications.

Lapox® C-51

Liquid液状

4.15-4.30

1300-1700

Max2

低粘度浇铸树脂,建议与胺类和聚肽胺类固化剂组合用于低压电器。Low viscosity reactive casting resin. Recommended with amine and polyaminoamide curing agents for low voltage electrical and electronic applications

Lapox® L-12

Liquid液状

5.25-5.40

10000-12000

Max2

多用途中粘度层压树脂,能与所有固化剂组合。General purpose medium viscosity laminating resin usable with all types of hardeners.

Lapox® L-43

Liquid液状

-------

3400-4200

Max2

低粘度低温固化层压树脂,用于涂层,但不适于直接接触食物和饮料。Low viscosity cold-curing laminating resin suitable for had lay up application. Not suitable for contact with foodstuffs or drinking water.

Lapox® L-137

Clear transparent Liquid 清澈半透明液状

5.2-5.5

450-650

------

低粘度多用途树脂,用于室温浇铸和层压。Low viscosity multipurpose resin used for casting or laminating at room temperature.

Lapox® T-23

Liquid液状

4.15-4.4

1300-1700

Max 2

与K-6固化剂组成层压树脂系统,与玻璃纤维一起用于浇铸模具的加强。With hardener K-6 is a laminating resin system designed mainly for use with glass-fibre for reinforcing foundry patterns foundry patterns, jigs and moulds.

Lapox® T-77

Paste 糊状

-----

------

-------

和K-25组成粘稠糊料。用在白粉上,能提高加工性。With hardener K-25 is a thick paste. Used over plaster of Paris for easy machinable property.

Lapox® T-73

White paste 白色糊状

-----

-----

-------

与K-73组成触变系统,形成一个白色低弹性边缘强硬的可加工凝胶涂层。With K-73 is a thixotropic system. Gives a white, slightly resilient, machinable gelcoat with good edge strength.

Lapox® T-96

Blue Paste 蓝色糊状

------

40000-65000

---------

与K-51组合为蓝色环氧涂层,非常耐磨,不易加工。With K-51 is a blue epoxy gelcoat with good abrasion resistance. It is very difficult to machine.

Lapox® T-22

Pale yellow浅黄色

4.15-4.40

1300-1700

Max 2

低粘度,室温固化胺类固化剂,特别用于浇铸模具的制作。Low viscosity, a room temperature curing amine hardener. Specially formulated filler is recommended for casting of patterns and moulds.

Lapox® T-94

Grey paste 灰色糊状

----

50000-100000

------

与K-53组成灰色金属填料树脂,有极强的表面强度。With K-53 is a metal filled grayish black epoxy resin, which gives a hard machinable surface on curing,.

Lapox® XR-27

Clear transparent liquid清澈半透明液状

4.9-5.2

4000-5500

Max - 2

与K-918组合用于达到H级的浇铸。Internally flexibilised epoxy resin for casting, potting with K-918 for upto Class H application.

Lapox® L-135

Low viscous clear liquid低黏度清澈液状

5.4-5.714

2400-2900

Max – 4

低粘度树脂,与K-552组合成一个室温固化系统,具有极其优良的机械和电性能,适合层压浇铸。Low viscosity epoxy resin. With hardener K-552 becomes a room temperature curing system, which offers excellent mechanical and electrical properties suitable for laminates, castings, with good anti-tracking properties.

Lapox® C-50

Clear transparent liquid清澈半透明液状

5.0-5.45

9000-14000

Max 3

与K-61组合成达到绝缘H级的组合。With K-61 for casting by pressure gelation suitable for class H insulation.

Lapox® P-1017

Pale yellow low viscosity clear liquid浅黄色低黏度透明液状

------

Max 50-500

Max 8

用于薄膜,抗酸,碱,洗涤剂,漂白粉,蒸汽等。Designed specially for decorative polyester films. Has excellent resistance to acids, solvents , alkalis, detergents, bleaching powder, steam etc.


Semi-Solid/Solid Epoxy Resins 半固状/固状环氧树脂

Name
品名

Description
状态

Epoxy Value
环氧值 eq/ kg

Viscosity Of 40% Solution in Butyl Carbitol
40%二甘醇一丁醚溶液中粘度 @ 25°C mPas

Softening Point
软化温度
(° C) (2)

Comments
注解

Lapox® P-3

Semi-Solid 半固态

2.15-2.22

160-190

65-75

与胺加合物及聚肽胺固化剂组合,生产溶剂型抗化学腐蚀油漆及船舶油漆。Recommended with amine adducts and polyaminoamide curing agents for solvent containing cold-curing chemical resistant coatings and marine paints.

Lapox® P-4

Solid 固态

1.12-1.20

550-700

90-102

建议与脂肪酸脂化,用于生产彩釉,即罐和管的外层涂料。Recommended for esterification with fatty acids for enamels and exterior coatings of cans and tubes

Lapox® P-5

Solid固态

0.53-0.59

1800-2600

110-120

建议与氨基改性酚醛树脂组合,生产罐的内层涂料。Recommended for cross linking with amino and phenolic resins as stoving lacquers for the internal coating of cans and tubes.

Lapox® P-6

Solid固态

0.34-0.42

5000-10000

125-140

高分子量,建议与氨基改性酚醛树脂组合,生产罐的内层涂料。Higher molecular weight recommended for cross linking with amino and phenolic resins stoving lacquers for internal coating of cans and tubes.

Lapox® P-10

Solid固态

1.08-1.18

430-550

90-100

建议脂化后用于阳极电极生产。Recommended for esterification to formulate water based systems for anodic electrodeposition.

Lapox® P-62

Solid固态

1.33-1.40

500-600

95-101

用于生产粉状涂料。Recommended for powder coatings formulations.

Lapox® P-304

Solid固态

1.0-1.15

750-1150

98-105

用于生产高强度粉状涂料。Recommended for the formulations of powders with good impact strength.

Name

品名

Description

状态

Epoxy Value

环氧值 eq/ kg

Viscosity

粘度

@ 25 °C mPas

Softening Point

软化温度

(° C)

Comments

注解

Lapox® P-71

Solid

1.68-1.75

300-360

75-85

高熔点树脂,用于提高粉状涂料的流动性和抗化学腐蚀能力。Higher melting point resin. Used in cold curing lacquers suitable for improving the flow properties and chemical resistance of epoxy powder coatings.

Lapox® P-76

Solid

1.15-1. 35

300-480

94-100

流动性控制。与P-62混合,能提高流动性。It is a master batch of flow control agent. It can be blended with Lapox P-62 to improve flow properties.

Lapox® P-127

Solid

1.08-1.20

450-600

85-95

建议与深颜色树脂混合,提高流动性。Recommended in hybrid systems with saturated polyesters., it has very good flow properties.

Lapox® P-682

Solid

1.6-1.9

1300-2500

92-98

高分子量树脂,用于钢筋涂料。High molecular weight epoxy resin for rebar coatings

Lapox® P-672

Solid

0.75-0.85

1070-2270

105-125

高分子量酚醛树脂,达到2.6。

High molecular weight Novolac modified resin with an average functionality of approx 2.6.

Name

品名

Description

状态

Epoxy Value

环氧值eq/ kg

Viscosity粘度 @ 120 °C mPas

Comments

注解

Lapox® B-7

Semi- Solid

3.57-4.45

450-800*

建议用于溶剂用量少的涂料。Resin recommended for low solvent coatings.

Lapox® C-1

Semi- Solid

2.44-2.63

370-490

建议与苯酐固化剂组合,用于高温(130度)抗老化的电子浇铸。Recommended with anhydride hardeners to make electrical castings with good aging resistance upto 130 deg c

Lapox® C-2

Semi- Solid

2.50-2.85

270-400

120度时,与C-1比较,反应时间缓慢,增长操作时间。Slow reactivity as compared to C-1 lower viscosity at the processing temperature of 120 deg c and gives longer pot life.

Lapox® C-59

Semi- Solid

2.60-2.9

300-400

与C-1比较,反应时间缓慢,增长操作时间。Slow reactivity as compared to C-2 gives longer pot life.

(*) 70% solution in Butyl carbitol at 25°C

 